Nylon 6 GF/PTFE
How to improve the wear resistance of nylon 6?
1. Adding glass fiber can significantly improve the mechanical strength and wear resistance of PA6, while enhancing its dimensional stability and heat resistance.
2. Adding PTFE to PA6 can significantly reduce the friction coefficient and improve wear resistance.
Maikesi uses a unique blending and compounding technology to add glass fiber and PTFE to PA66, which significantly improves wear resistance and self-lubricating properties.
Product name: PA6-GF10-PTFE
Material characteristics:
10% glass fiber reinforced nylon 6; adding PTFE to improve wear resistance and lubricity; excellent flow ability; high dimensional stability; good impact resistance; good scratch resistance
Applications of PA6-GF-PTFE: mechanical engineering; vehicles; slides
Typical Data Sheet：
|
ITEM（23℃） |
METHOD |
UNIT |
Test Data |
|
Physical and chemical properties |
|||
|
Density |
ISO 1183 |
g/cm³ |
1.25 |
|
Molding shrinkage |
ISO 294-4 |
% |
0.3-0.5 |
|
Flammability rating |
UL-94 |
Class |
HB |
|
Mechanical properties |
|||
|
Tensile Strength |
ISO 527 |
MPa |
110 |
|
Elongation at break |
ISO 527 |
% |
4.5 |
|
Bending strength |
ISO 178 |
MPa |
170 |
|
Flexural modulus |
ISO 178 |
MPa |
2145 |
|
Charpy Impact Strength(Notched) |
ISO 179 |
kJ/m² |
5.5 |
|
Charpy Impact Strength |
ISO 179 |
kJ/m² |
62 |
|
Thermal properties |
|||
|
HDT（1.82MPa） |
ASTM D648 |
℃ |
210 |
|
Injection molding process |
|||
|
Pre-drying |
temperature |
℃ |
80-120 |
|
Time |
h |
4-5 |
|
|
Mold temperature |
80-90℃ |
||
|
Barrel temperature |
Front temperature |
Processing temp |
Rear temperature |
|
240-245℃ |
240-250℃ |
230-240℃ |