Polyamide thermoplastic high performance polymer (PA12) for injection molding
Maikesi's PA12 includes various versions: transparent, glass fiber or carbon fiber reinforced（PA12 GF,PA12 CF）
Adapting to different formulations, PA12 can be processed using a range of different methods such as injection molding, pipe extrusion, film extrusion or blow molding.
Compared with 956, 926 has more cost advantages.
Product name: PA12 926
PA12 Material characteristics:
Long Carbon Chain Nylon.Low density, High resilience; Extremely low water absorption; Chemical resistance; High transparency; Good dimensional stability; High temperature resistance
Applications of Nylon 12: Pumps, valves, sanitary components, automobiles, bearings
Typical Data Sheet：
|
ITEM |
METHOD |
CONDITION |
UNIT |
Test Data |
|
Physical and chemical properties |
||||
|
Density |
ISO 1183 |
23℃ |
g/cm³ |
1.02 |
|
Melt flow rate |
ISO 11357 |
- |
g/ min |
3 |
|
Transmittance |
- |
- |
% |
≥92 |
|
Saturated water absorption |
ISO 62 |
- |
% |
3 |
|
Molding shrinkage |
ISO 294 |
3.2mm |
% |
0.4-0.5 |
|
Flammability rating |
UL-94 |
1.6mm |
Class |
HB |
|
Mechanical properties |
||||
|
Tensile Strength |
ISO 527 |
50mm/min |
MPa |
62 |
|
Elongation at break |
ISO 527 |
50mm/min |
% |
170 |
|
Flexural strength |
ISO 178 |
2mm/min |
MPa |
72 |
|
Flexural modulus |
ISO 178 |
2mm/min |
MPa |
1580 |
|
Charpy Impact Strength(Notched) |
ISO 179 |
23℃ |
kJ/m² |
18 |
|
Thermal properties |
||||
|
HDT（1.8MPa） |
ISO 75-2 |
120℃/H |
℃ |
105 |
|
Flammability |
UL94 |
1.6mm |
class |
HB |
|
Injection molding process |
||||
|
Pre-drying |
temperature |
- |
℃ |
90-110 |
|
Time |
- |
h |
4-8 |
|
|
Mold temperature |
60-120℃ |
|||
|
Barrel temperature |
Front temperature |
Processing temp |
Rear temperature |
|
265-275℃ |
255-265℃ |
230-240℃ |
PA12 is transparent nylon,has the characteristics of Low density, High resilience; Extremely low water absorption; Chemical resistance; High transparency; Good dimensional stability; High temperature resistance, etc.