PA6I-2098
Polyamide thermoplastic high performance polymer (PA6I) for injection molding
PA6I is a nylon material that belongs to the polyamide family of plastics. It is a thermoplastic polymer made by the polymerization of adipic acid and caprolactam. PA6I has excellent physical and mechanical properties, making it very popular in many industrial applications.
Compounding PA6I with PA66/6 can also significantly improve the chemical resistance and appearance of the product.
Product name: PA6I
PA6I Material characteristics:
Low warpage, High barrier properties; low water absorption; Chemical resistance; High transparency; Good dimensional stability.
Typical Data Sheet：
|
ITEM |
METHOD |
CONDITION |
UNIT |
Test Data |
|
Physical and chemical properties |
||||
|
Density |
ISO 1183 |
23℃ |
g/cm³ |
1.18 |
|
Melt flow rate |
ISO 11357 |
- |
g/ min |
4 |
|
Transmittance |
- |
- |
% |
≥85 |
|
Saturated water absorption |
ISO 62 |
- |
% |
2 |
|
Molding shrinkage |
ISO 294 |
3.2mm |
% |
0.6-0.7 |
|
Flammability rating |
UL-94 |
1.6mm |
Class |
HB |
|
Mechanical properties |
||||
|
Tensile Strength |
ISO 527 |
50mm/min |
MPa |
90 |
|
Elongation at break |
ISO 527 |
50mm/min |
% |
50 |
|
Flexural strength |
ISO 178 |
2mm/min |
MPa |
120 |
|
Flexural modulus |
ISO 178 |
2mm/min |
MPa |
3100 |
|
Charpy Impact Strength(Notched) |
ISO 179 |
23℃ |
kJ/m² |
9 |
|
Thermal properties |
||||
|
HDT（1.8MPa） |
ISO 75-2 |
120℃/H |
℃ |
110 |
PA6I is an aromatic nylon with low warpage, high barrier properties; low water absorption; chemical resistance; high transparency; good dimensional stability, etc. It is suitable for nylon modification.